Concrete has the innate ability to shrink. Concrete shrinkage meaning is the volume changes that are seen in concrete as a result of moisture loss occurring at various stages for various reasons.
Shrinkage is a natural and inevitable process that occurs in a wide variety of materials, including concrete, plastic, and wood. It is a result of the physical and chemical changes that occur during the drying, cooling, or curing of these materials, which cause them to contract and shrink in size.
While shrinkage is often unavoidable, it can have significant consequences, including cracking, distortion, and reduced durability. As a result, understanding the causes and effects of shrinkage is crucial for engineers, architects, and manufacturers seeking to produce high-quality, reliable products and structures. This article will explore the phenomenon of shrinkage, its underlying mechanisms, and some of the methods used to mitigate its effects.
Different forms of concrete shrinkage
Plastic shrinkage in concrete
Source: Pinterest
After the concrete is cast, it is seen that the process of evaporation from the structure’s surface causes water needed for concrete strength gain to escape into the atmosphere. The surface of the structure will develop fractures as a result of this. Water absorption from the concrete by the aggregate is another cause of shrinkage cracks under the plastic shrinkage type.
Due to the reinforcement or aggregate particles getting in the path of subsidence, fractures may develop on the structure’s outside or internally around the aggregates. When exposed to the sun and drying winds, the surface area of floors and pavements is exposed to drying to a greater degree than the depth, which causes the plastic to shrink as the surface dries out fast. There is a chance that excessive water channels might lead to bleeding in a mixed design where the water-cement ratio is high. The extra water from the bleeding will build up on the slabs’ surface. These develop cracks when exposed to dry weather because the surface dries off.
What influences concrete shrinkage from plastic?
To stop the cause of plastic shrinkage, employ the following remedies:
- Polyethylene sheeting can be used to cover the surface to stop water from evaporating from it. Shrinkage of plastic may be avoided by preventing water evaporation.
- Shrinkage of the plastic can be avoided by properly vibrating the concrete.
- Utilising aluminium powder can help concrete constructions experience less plastic shrinkage.
- Plastic shrinkage can also be managed with the use of expansive cement.
Drying shrinkage
Source: Pinterest
Drying shrinkage is a result of the loss of hydrostatic tension in the microscopic pores and the surface-absorbed water from the calcium silicate hydrate (C-S-H) gel. The reverse of shrinking is a process known as swelling. Although the aggregate stiffness has an impact, the deformation of the paste is the primary cause of this shrinkage. The drying shrinkage that occurs after the concrete has hardened is referred to as such. The majority of drying shrinkage occurs during the first few months a concrete structure is in use. Drying shrinkage is brought on by the removal of water from the concrete that has been held in the unsaturated air spaces. By submerging the concrete in water for a certain amount of time, some of the shrinkage induced can be restored. The moisture movement is what is meant by this.
What influences concrete shrinkage after drying?
The key elements that influence drying shrinkage are as follows:
- Material selection: To reduce the likelihood of drying shrinkage, high-quality ingredients must be included in the concrete mix. The qualities and specifications of the ingredients must adhere to the local region’s standard norms.
- Water-to-cement ratio: The likelihood of drying shrinkage increases as the water-to-cement ratio in the concrete mix increases. The paste’s strength and overall stiffness will decrease as the water-to-cement ratio rises. As a result, shrinkage rises as water content rises.
- Environmental factors: The drying shrinkage of the concrete building is significantly influenced by the relative humidity of the location. Reduced shrinking is associated with a rise in the humidity of the surrounding air.
- Content of cement: As the amount of cement in the mixture increases, the rate of shrinkage will also rise.
- The type of aggregates utilised in the mix: Aggregate size will have an impact on the reason for drying shrinkage. The shrinking will be reduced by raising aggregate maximum sizes. The shrinkage properties of concrete are not significantly influenced by the grading or form of the aggregate. Aggregates with a high degree of surface roughness will resist shrinking.
Concrete autogenous shrinkage
Source: Pinterest
Even after the concrete structure has been set, volume changes continue to occur. The volume under consideration might either decrease or grow. When water is accessible, maintaining hydration is much easier. This may lead to the concrete structure’s enlargement. However, when there is not enough moisture to carry out this hydration, the concrete swells. Therefore, this kind of shrinkage occurs as a result of water being drawn out of the concrete’s capillary pores. This water outflow is caused by the hydration process. The hydration of hydrated cement depends on water. Self-desiccation is the term for the process of removing water from capillary pores in order to hydrate cement. Autogenous shrinkage or autogenous volume change are two terms that describe the shrinkage that is dealt with by such a conservative system.
What influences concrete autogenous shrinkage?
- Thermostat: The rate of autogenous shrinkage, which is connected to the hydration process, will increase as the temperature rises, causing a greater volume change.
- Cement content: The amount of cement in the mixture affects how much shrinkage occurs naturally. No matter how much water is in the mix, the cement will still be hydrated through a process called hydration. Hydration will increase with cement content. Therefore, the volume change caused by shrinking will rise.
- The cement’s chemical makeup: The autogenous shrinkage will be accelerated by some types of cement that include high concentrations of tetra calcium alumino ferrite (C4AF) and tricalcium aluminate (C3A). These unique mixtures encourage the creation of more hydration products.
- Mixtures of minerals: Mineral admixtures will speed up the hydration process and, in turn, cause more autogenous shrinkage. For instance, the increased surface area of a mineral admixture like fly ash supports increased reactivity and high-quality hydration products. More water will be required from the capillary pores as a result. As a result, the concrete’s volume changes more as a result of shrinkage.
Concrete shrinkage due to carbonation
Source: Pinterest
The likelihood of a reaction between carbon dioxide and the concrete poured is increased. Moisture is required for this reaction to occur. The carbonates will develop as a result of this. The concrete contains a significant amount of calcium hydroxide, a byproduct of the hydration cycle. When this calcium hydroxide and carbon dioxide in the air interact, calcium carbonates are produced. This will cause the concrete surface to change and take on an acidic or carbonated character. This process is referred to as carbonation. Shrinkage results from this, which is visible on the surface. It could be seen while the concrete building is still in use. In locations with circumstances of intermediate relative humidity, carbonation shrinkage is seen.
What influences concrete shrinkage due to carbonation?
- Cement type: The type of cement used in the concrete mixture can affect carbonate shrinkage. Portland cement is more prone to carbonate shrinkage than blended cement, which contains a lower percentage of calcium hydroxide.
- Water-cement ratio: The water-cement ratio of the concrete mixture can affect the rate of carbonate shrinkage. A high water-cement ratio can increase the amount of moisture available for the carbonation reaction, which can lead to more shrinkage.
- Aggregate type: The type of aggregate used in the concrete mixture can affect carbonate shrinkage. Aggregates that contain carbonates, such as limestone, can increase the rate of carbonation and shrinkage.
- Exposure conditions: The exposure conditions, such as temperature and relative humidity, can affect the rate of carbonation and shrinkage. Higher temperatures and lower relative humidity can accelerate the carbonation reaction, while lower temperatures and higher relative humidity can slow it down.
- Curing: The curing conditions of the concrete can also affect carbonate shrinkage. Adequate curing, which involves keeping the concrete moist and protected from the elements, can slow down the carbonation reaction and reduce shrinkage.
FAQs
What is shrinkage in concrete?
Shrinkage in concrete refers to the reduction in the volume of concrete as it dries and cures over time. This shrinkage can cause cracking and loss of strength and is a common problem in concrete construction.
What causes shrinkage in concrete?
Shrinkage in concrete is caused by a number of factors, including the loss of moisture, the reaction of carbon dioxide with calcium hydroxide, and the chemical reactions that occur as the concrete cures and hardens.
How can shrinkage in concrete be prevented?
Shrinkage in concrete can be prevented or reduced by controlling the water-cement ratio of the mixture, ensuring adequate curing, and using a low-shrinkage concrete mix.